Nano Bonded Refractory Materials - Mathios Refractories

PRODUCT NAME	Classification Temperature. _{(EN 1402-1) at ^oC}	Main Raw Material Base _{(EN 1402-1)}	_{Chemical Analysis(%) (EN ISO 12677)} Al₂O₃	_{Chemical Analysis(%) (EN ISO 12677)} SiO₂	_{Chemical Analysis(%) (EN ISO 12677)} Fe₂O₃	_{Chemical Analysis(%) (EN ISO 12677)} ZrO₂	_{Chemical Analysis(%) (EN ISO 12677)} SiC	_{Chemical Analysis(%) (EN ISO 12677)} BaO	Bulk Density _{(EN 1402-6) at 110^oC (g/cm³)}	C.C.S. _{(N/mm²) (EN 1402-6)} at 110^oC	C.C.S. _{(N/mm²) (EN 1402-6)} at 800^oC	C.C.S. _{(N/mm²) (EN 1402-6)} at 1100^oC	C.C.S. _{(N/mm²) (EN 1402-6)} at 1500^oC	Thermal Conductivity _{(W/mK) (EN 993-14) at 800^oC}	Grain Size _{(mm) (EN 1402-3)}	Permanent Linear Change(%)_{(EN 1402-6)} at 110^oC	Permanent Linear Change(%)_{(EN 1402-6)} at 1100^oC	Permanent Linear Change(%)_{(EN 1402-6)} at 1500^oC	Material required (kg/m³)	Reversible thermal expansion at 1000^oC(%)	Approx. Water addition _{(EN 1402-4) (lt/100kg dry material)}
MAT NANO 60-M	1650	Sintered Mullite	> 61,0	34.0	1.0	-	-	-	2.40	28	80	80	90	1.73	6	-	-0.40	-0.7	2570	0.62	6,5 -- 7,0
MAT NANO 70-M	1650	Sintered Mullite	> 69,0	27.0	1.0	-	-	-	2.50	30	70	75	80	1.78	6	-	-0.45	-0.85	2570	0.65	6,5 -- 7,0
MAT NANO 85	1600	Bauxite	> 84,0	10.6	1.6	-	-	-	2.75	30	70	90	90	2.32	6	-	-0.60	-	2800	0.70	6,5 -- 7,0
MAT NANO 80-AL	1300	Bauxite	>80,0	10.8	1.5	-	-	2.5	2.74	28	70	90	-	2.32	6	-	-0.50	-	2810	0.70	6,5 -- 7,0
MAT NANO 90-AL	1300	Sintered Alumina	>88,0	0.5	0.1	-	-	6.0	3.30	25	60	70	-	2.41	6	-	-0.50	-	3100	0.72	6,5 -- 7,0
MAT NANO 55-M SIC10	1500 (red)	Sintered Mullite - SiC	> 55,0	31.0	0.9	-	> 9,5	-	2.38	28	65	80	80	3.48	6	-	-0.30	-	2430	0.60	6,5 -- 7,0
MAT NANO 25SIC-M	1500 (red)	Sintered Mullite - SiC	47.5	27.0	0.9	-	> 24,0	-	2.48	25	60	70	80	4.1	6	-	-0.30	-	2540	0.58	6,5 -- 7,0
MAT NANO ZS 10-M	1500 (red)	Synthetic Raw Materials	> 54,0	25.0	0.8	> 9,5	> 9,5	-	2.62	28	70	80	80	3.46	6	-	-0.10	-	2670	0.58	6,5 -- 7,0