Micron Ultra Low Cement Castables - Mathios Refractories

PRODUCT NAME	Classification Temperature. _{(EN 1402-1) at ^oC}	Main Raw Material Base _{(EN 1402-1)}	_{Chemical Analysis(%) (EN ISO 12677)} Al₂O₃	_{Chemical Analysis(%) (EN ISO 12677)} SiO₂	_{Chemical Analysis(%) (EN ISO 12677)} Fe₂O₃	_{Chemical Analysis(%) (EN ISO 12677)} ZrO₂	_{Chemical Analysis(%) (EN ISO 12677)} SiC	_{Chemical Analysis(%) (EN ISO 12677)} BaO	Bulk Density _{(EN 1402-6) at 110^oC (g/cm³)}	C.C.S. _{(N/mm²) (EN 1402-6)} at 110^oC	C.C.S. _{(N/mm²) (EN 1402-6)} at 800^oC	C.C.S. _{(N/mm²) (EN 1402-6)} at 1100^oC	C.C.S. _{(N/mm²) (EN 1402-6)} at 1500^oC	Thermal Conductivity _{(W/mK) (EN 993-14) at 800^oC}	Grain Size _{(mm) (EN 1402-3)}	Permanent Linear Change(%)_{(EN 1402-6)} at 110^oC	Permanent Linear Change(%)_{(EN 1402-6)} at 1100^oC	Permanent Linear Change(%)_{(EN 1402-6)} at 1500^oC	Material required (kg/m³)	Reversible thermal expansion at 1000^oC(%)	Approx. Water addition _{(EN 1402-4) (lt/100kg dry material)}
MAT MICRON 60-M	1650	Sintered Mullite	> 60,0	33.5	1.0	-	-	-	2.50	60	90	100	120	1.75	6	-	-0.30	-0.05	2580	0.65	4,0 - 4,8
MAT MICRON 60-A	1670	Andalusite	> 60,0	36.5	0.7	-	-	-	2.64	70	75	90	100	1.75	6	-	0.25	-	2700	0.65	4,0 - 4,8
MAT MICRON 80-E	1650	Bauxite	> 80,0	13.0	1.4	-	-	-	2.80	75	120	125	135	2.23	6	-	-0.35	0.20	2860	0.72	4,2 - 4,8
MAT MICRON 80	1620	Bauxite	> 80,0	11.0	1.5	-	-	-	2.87	75	100	125	135	2.25	6	-	-0.40	-0.70	2940	0.68	4,2 - 4,8
MAT MICRON 80-AL	1320	Bauxite	> 80,0	10.2	1.4	-	-	2.5	2.83	65	100	120	-	2.24	6	-	-0.30	-	2890	0.72	4,0 - 4,8
MAT MICRON 55 A SIC7	1530 (red)	Andalusite - SiC	> 55,0	33.0	0.7	-	7.0	-	2.68	60	85	90	90	2.68	8	-	0.50	-	2740	0.63	4,0 - 4,8
MAT MICRON 55 M SIC10	1530 (red)	Sintered Mullite - SiC	> 55,0	30.5	0.9	-	> 9,5	-	2.55	60	90	110	110	3.50	6	-	-0.25	-	2620	0.60	4,0 - 4,8
MAT MICRON 10 ZS-M	1230 (red)	Synthetic Raw Materials	> 52,0	24.5	0.8	> 9,7	> 9,5	-	2.72	60	90	110	110	3.45	6	-	-0.25	-	2770	0.58	4,0 - 4,8